HPM50CMC hardfacing wire series argon fill mode 


 CMC-SKD11-3 

 Hardness HRC56 ~ 58 

 1.2 1.6 2.4 

 Cold welding steel, die, die cutting, cutting tools, molding, hard surface parts production, high hardness, wear resistance and high toughness of argon welding. 


 CMC-SKD61-2 

 Hardness HRC52 ~ 57 

 1.0 1.2 


 1.6 2.4 3.2 

 Welding hot forging die, eager die, hot punch, thermo-forming mold, hot tools, die steel. 


 CMC-SKD61 

 Hardness HRC42 ~ 46 

 1.2 1.6 2.4 

 Welding aluminum and copper die-casting mold, with good heat resistance, wear resistance, cracking resistance. 


 CMC-SKD61-42 

 Hardness HRC42 ~ 48 

 1.6 

 Welding hot forging die, forging die of aluminum copper, aluminum and copper die-casting mold, with good heat resistance, wear resistance, cracking resistance. 


 CMC-8407-H12 

 Hardness HRC52 ~ 57 

 1.0 1.2 1.6 2.4 

 Welding hot forging die, eager die, hot punch, thermo-forming mold, hot tools, die casting mold steel. 


 CMC-8407 

 Hardness HRC40 ~ 45 

 0.9 1.2 1.6 2.4 

 Welding zinc, aluminum, tin and other non-ferrous alloy and copper alloy die casting mold. 


 CMC-M3-2 

 Hardness HRC61 ~ 63 

 1.2 1.6 2.4 

 Supplemented module Broach, hot hardness tool dies, the total die forging, hot die, screw die, hard surface wear, high-speed steel. 


 CMC-MS-3 

 Hardening 500 ° 2H 


 Hardness HRC48-50 

 1.2 1.6 2.0 2.4 

 Special hardened high toughness alloy is very suitable for aluminum gravity die-casting mold, the gate to extend the service life of 3 to 5 times, mold can be made very precise, super-mirror (gate repair welding, the use of thermal fatigue cracks is not easy) 


 CmC-12Cr 

 Hardness HRC53 ~ 57 

 1.0 1.2 1.6 


 2.4 3.2 

 Dedicated to Cr12, Cr12MoV series of mold repair argon welding. 
 For the heat treatment before machining can be heat treatment, heat treatment, dimensional change is small, easy to crack. If required to weld up more than 3 layers, available CMC-30N rendering. For heat treatment of Cr12, a small area from time to warm up. Melting sufficient hardness can be machined. 


 CMC-Magic1 

 Hardness after hardening 


 HRC50 ~ 54 



 1.0 1.2 1.6 2.4 



 Extremely easy to crack, can be heat treated high carbon steel 
 Melting fine for the tensile modulus can significantly reduce the high tension steel and general steel bending, stretch forming scratches when