Co101 Cobalt Electrode 

 For high-temperature hardness, strong abrasive wear and corrosion resistance. For rotary sealing rings, roller bearings, sleeve, drill and so on. 

 Co104 Cobalt Electrode 

 Stellite cobalt electrode 4 

 For high wear resistance, excellent high temperature strength and corrosion resistance. For copper, aluminum heat dies, hot extrusion die, die, etc. batteries. 

 Co106 Cobalt Electrode 

 Cobalt-based Stellite 6 electrode 

 Better wear resistance, high temperature, thermal shock, anti-scratch performance. For engine valves, high temperature and high pressure valve sealing surface, hot shear blades, turbine blades and so on. 

 Co112 Cobalt Electrode 

 Stellite 12 cobalt-based electrodes 

 High wear resistance, corrosion resistance to abrasion performance. For high temperature, high pressure valves, cutting blades, serrated, spiral Putters. 

 D968 high temperature electrode wear 
 : Graphite coating of the welding electrodes, AC and DC. Deposited metal hardness HRC: 61 ~ 66. 
 Cobalt Hardfacing Wire Description: welding D802 tungsten wire welded cobalt-chromium casting core welding wire, solder dipping into the legal system with a core surfacing wire, deposited metal at 1000 ℃, which still has a good rose about turbulent バO read through  onions Meng Jing S archery Holland Mi sense of shame, as the dogs howl bribe bang bang  cattle  trouble cub Mei Gong Zi Zi-e port turbulence  tragic song about Ang Pu Fu angry pocket of zinc's long and floating charge acres of acetylene bad lessons: Fu E Mengchia  С ghosts fluttering of flag Zheng ǎ ィ 〤 1.0 ~ 1.7 Cr 26.0 ~ 32.0 W 7.0 ~ 10.0 Mn ≤ 2.0 Si ≤ 2.0 Fe ≤ 3.0 Co margin surfacing hardness HRC ≥ 40 specifications φmm 2.5 3.0 D802D812D822D842 ECoCr-cobalt-based electrodes A cobalt-based electrodes 
 Cobalt-based electrodes 

 D802 cobalt-based electrodes 
 Model: GB / T EDCoCr-A-03 rather: AWS ECoCr-A JIS DF-CoCrA 
 Description: cobalt chromium tungsten alloy cobalt-based hardfacing welding rod core, the use of DCRP, deposited metal work at 650 ℃ can maintain good wear resistance and corrosion resistance. 
 Use: about 650 ℃ work can still maintain good wear resistance and corrosion resistance of the occasion, or to withstand shocks and hot and cold cross the site, such as the welding temperature and high pressure valves and thermal cutting edge and so on. 
 Surfacing hardness HRC: ≥ 40 

 D812 cobalt-based electrodes 
 Model: GB / T EDCoCr-B-03 rather: AWS ECoCr-B JIS DF-CoCrB 
 Description: cobalt chromium tungsten alloy cobalt-based hardfacing welding rod core, the use of DCRP, deposited metal work at 650 ℃ can maintain good wear resistance and corrosion resistance. 
 Application: high temperature and pressure valves, high pressure pump shaft sleeve and inner sleeve and the blade cut fiber port and other equipment. Surfacing hardness HRC: ≥ 44 

 D822 cobalt-based electrodes 
 Model: GB / T EDCoCr-C-03 rather: AWS ECoCr-C JIS DF-CoCrC 
 Description: The high-carbon cobalt-chromium alloy welded tungsten welding electrode core cobalt-based, using DC reverse, slag coverage is good, beautiful appearance, with excellent wear resistance, heat resistance, corrosion resistance, high temperature at 650 ℃ can be maintained these characteristics. 
 Uses: cone bit bearing, rotating impeller boilers, mill edge, wear parts such as screw feeder surfacing. 
 Surfacing hardness HRC: ≥ 53 

 D842 cobalt-based electrodes 
 Model: GB / T EDCoCr-D-03 pretty: JIS DF-CoCrC 
 Description: 4 low-carbon cobalt-based cobalt chromium tungsten alloy core welding electrode welding, the use of DCRP, deposited metal can be maintained even at 800 ℃, thermal fatigue and corrosion resistance. 
 Uses: Used to withstand impact and high temperature conditions, hot and cold welding parts staggered, such as hot forging die, the valve sealing surface, with good performance. 
 Surfacing hardness HRC: 28-35 
 D852 Cobalt Electrode Type: EDCoCr-E-04 

 Description: wear welding electrodes for high temperature, the working temperature 1100 ℃, with the red hardness, strong resistance. Also be used for high temperature, high pressure valves and other hot leg model, while subjected to impact and high temperature, corrosion resistant components. HRC ≥ 44 

 D862 Cobalt Electrode Type: EDCoCr-E-05 

 Description: suitable for high temperature wear and fine grinding of small-angle erosion conditions. Single-layer surfacing to meet the performance requirements, the maximum operating temperature 1000 ℃, surfacing layer hardness: 20 ℃ - HRC :64-66, working temperature 600 ℃ - HRC :48-52, working temperature 800 ℃ - HRC :38-42 Typical application areas, and some conditions, iron, coke, clean burning, high-temperature cement and other areas of work wear and tear of machinery and equipment there. 

 Uses: serving under the high temperature part for welding clean burning crown single roll crusher and blast furnace grate rotary distribution chute, wear results are obvious.