ER5183 aluminum-magnesium alloy wire 
 Features: This product is 3% of magnesium alloy welding wire for welding or surfacing material with the level of aluminum. 
 Uses: Chemical pressure vessels, nuclear industry, shipbuilding, refrigeration industry, boiler, aerospace industry, etc. 
 ER2319 aluminum-copper alloy wire 
 Features: This product is 5.8% -6.8% copper alloy welding wire for welding the same level of aluminum alloy 2219. 
 Uses: nuclear industry, ship manufacturing, aerospace industry, military equipment, etc. 
 HS301 aluminum wire 

 ER1060 Aluminum Welding Wire | 

 ER1100 aluminum welding wire 

 JIS A1100 
 Description: HS301 is larger than 99.5 of the aluminum wire aluminum, has a good weldability and corrosion resistance, and excellent ductility and toughness, but lower strength. 
 Uses: Suitable for welding and oxygen - acetylene gas welding aluminum and less demanding on the joints of aluminum alloy as a filler material, aluminum is widely used in chemical industry equipment. 
 Chemical composition (%) 
 Si Fe Al ≤ 0.3 ≤ 0.3 ≥ 99.5 Mechanical Properties of Deposited Metal (use aluminum as a docking test board) 
 Pilot project σb (MPa) cold (D = 2T) degrees to ensure that the value of ≥ 64 - 69 ~ 78 180 general results of standard wire 
 Diameter (mm) 
 φ1.0 φ2.0 φ3.0 φ4.0 φ5.0 φ6.0 
 Length (mm) ring mounted 1000 
 Note: 
 1. Should be strictly removed before welding and wire welding the edge of the surface oxide film and the oil, otherwise it would be bad and cause weld porosity produced fusion, slag and other defects. 
 2. Hold the welding molten metal plate can be used to ensure that the weld shape.