 Description: D132 titanium calcium type of CrMo-type welding electrode. AC-DC dual-use, when welding arc stability, easy slag removal. 

 Uses: used in the wear of low carbon steel, medium carbon steel and low alloy steel parts surface, especially suitable for mining machinery and agricultural machinery and repair welding of wear parts. 

 Chemical Composition of Deposited Metal (%) 
 Chemical composition of C Mo Cr 
 Guaranteed value ≤ 0.50 ≤ 1.50 ≤ 3.00 


 Surfacing layer hardness: HRC ≥ 30 

 Reference current (AC, DC) 
 Electrode diameter (mm) φ3.2 φ4.0 φ5.0 φ5.8 
 Welding current (A) 80 ~ 130 110 ~ 180 150 ~ 240 240 ~ 280 


 Note: 
 1. Welding electrodes shall be subject to 150 ℃ or so before baking 1h. 
 2. In large parts prior to welding should be properly preheated to about 300 ℃, and welding parts of the surface rust and oil removed.