YST132 high manganese steel electrodes integrated 

 Description: YST132 base xingyao rutile coated electrode is 160% high deposition efficiency, deposition of metal for high-Mn austenitic stainless steel. Mn steel used in welding and in (14% Mn) on the shoe together, for different welded joints and difficult welding materials. Do buffer layer before hardfacing and repair worn parts from the vibration. 

 Uses: used rail, excavators, cement industry, the maintenance of different types of crushing machines. 

 Base material: shielding steel, tool steel 

 Austenitic steels with Mn: type Z120 M 12, X120 Mn 12, 1.3401 

 Spring steels: 45 Cr4, 1.7035,46 Si 7,1.5024,51 Si 7,1.5025,56 Si 7,1.5026 

 Mechanical Properties: 

 General results of the pilot project 

 Tensile strength σb (MPa) 600-750 

 Yield strength σs (MPa)> 400 

 Elongation δ5 (%)> 30 

 Impact energy AKV (J) + 20 ℃ when> 70 

 200 HB hardness after welding 

 Processing hardness HB 500 

 Chemical composition (%): 

 C Mn Si Ni Cr 

 0.1 5.00 0.80 8.50 18.00 

 Packaging data: 

 Standard 

 Quasi- 

 Package 

 Installation dimensions (mm) 2.5 × 350 3.2 × 350 4.0 × 450 

 Number of 444 per bag 

 Each package (Lbs) 9.9 11 14.3 

 Carton Weight (Lbs) 3.6 44 57.2 

 Reference current: 

 Ampere (A) 90 130 160 

 Note: need to dry at 250 ℃ for 2 hours.